Metod
|
Kalınlık mm
|
Farklı kalınlık. birleş.
|
Yüzey paslı-tufallı
|
S.çelik
|
P.çelik
|
Alüm.
|
Bakır
|
Gaz tavsiyesi
|
TIG
|
1-6
|
+
|
+
|
+
|
+
|
+
|
+
|
Argon
|
TIG
|
1-6
|
|
|
|
+
|
|
|
ARGOHİD 2 ARGOHİD10 ARGOHİD15
|
TIG
|
1,5-6
|
+
|
+
|
|
|
+
|
+
|
ARK-50 ARK-75
|
MIG/MAG
|
1-6
|
|
|
|
|
+
|
+
|
Argon
|
MIG/MAG
|
6-12
|
|
|
|
+
|
+
|
+
|
ARK-25
|
MIG/MAG (kd,spa,dar)
|
1,5-12
|
|
+
|
+
|
|
|
|
ARCO-2 ARCO-5 ARCO-10
|
MIG/MAG (kd,spa,dar)
|
1,5-12
|
+
|
+
|
+
|
|
|
|
HB-205 HB-212
|
MIG/MAG (kd,spa,dar)
|
1,5-12
|
|
+
|
+
|
|
|
|
ARK-HeC
|
MIG/MAG (kd,spa,dar)
|
12 den büyük
|
+
|
+
|
+
|
|
|
|
HB 220
|
MIG/MAG (kd,spa,dar)
|
1-6
|
+
|
|
|
+
|
|
|
ARK-HeS1
|
MIG/MAG (kd,spa,dar)
|
6-12
|
+
|
|
|
+
|
|
|
ARCO-2
|
MIG/MAG (spa,dar)
|
1,5-6
|
+
|
|
+
|
|
|
|
ARO-2 ARO-5
|
MIG/MAG (spa,dar)
|
1,5-6
|
|
|
+
|
+
|
|
|
ARO-1 ARO-2
|
MIG/MAG (kd)
|
1,5-6
|
|
|
+
|
|
|
|
ARCO-18 ARCO-25
|
MIG/MAG (kd)
|
1-6
|
|
|
|
+
|
|
|
ARK-HeS2
|
MIG/MAG (i.damla)
|
1,5-6
|
|
|
+
|
|
|
|
CO2 ARCO-18 ARCO-25
|
FCAW (i.damla)
|
1,5-6
|
+
|
|
+
|
+
|
|
|
ARCO-10 ARCO-18 ARCO-25
|
FCAW (i.damla)
|
1,5-12
|
+
|
+
|
+
|
|
|
|
CO2
|
kd: kısa devreli geçiş
|
||||||||
spa: spray ark geçiş
|
||||||||
dar: darbeli ark geçiş
|
||||||||
i.damla: iri damlacık geçiş
|
||||||||
GENEL KURAL: 1mm.den ince malzemelerin kaynağında en uygun netice için TIG metodu kullanılır.Daha kalın malzemelerin kaynağında, genellikle ekonomik olan MIG/MAG metodu tercih edilir. Özellikle galvanizli, paslı, tufallı yüzeyli ve / veya farklı kalınlıklarda birleştirilecek çeliklerin hızlı kaynağında FCAW (özlü tel ile ark kaynağı) tercih edilir.
|